PU-Rubbers

PU-Rubbers

The workhorses in mold making. These rubbers give you bang for your buck. Solid performing, shrink free mold rubbers that will last forever casting concrete, gypsums, resins etc.



PU rubber products

Brush-On 35 Strong, durable, easy to mix, quick to work with -- practically no shrinkage !



Clear Flex series absolute clarity and resistance to sunlight. Low viscosity ensures easy mixing and pouring



Econ 80 is an economical Shore 80A polyurethane rubber. It is a lower cost, faster cure alternative to our popular PMC®-780.



PMC-121 series easy to mix - 1A:1B - high performance for gypsum and concrete



Vytaflex series easy to mix - 1A:1B - high performance for gypsum and concrete



PMC-Series somewhat harder PU-rubbers, traditionally used in the ceramic and concrete industry



Simpact 85A fast-setting Shore 85A urethane with high tear strength, impact resistance.



UreCoat - Flexible Coating can be mixed and brushed for a flexible, tough and impact resistant coating.





PU-Additives & Accessoires

SO-Strong tints can be used to create a variety of color effects for a wide range of material applications



Ignite tints liquid fluorescent colorants compatible with urethanes and silicones.



Cryptolyte a liquid to give cured silicones, pu-rubbers, plastics and foams a bright blue glow under ultra violet light



Kick-iT Accellerator designed to "accelerate" the cure time of some urethane liquid rubber products



SO-Flex is a softening agent that will lower the cured durometer of a variety of flexible polyurethane products.



SO-Cure accelerates the cure time of urethane resins without significantly affecting physical properties.



Sun Devil to slow color change and physical degradation due to UV exposure for many liquid urethanes



Double Coat Two component high filling polyurethane varnish. Gloss. Easy application by brush or roller.



Watertrap Watertrap Potassium Silicate for pouring urethanes into waterbased moulds





Clear Flex Series

Clear-Flex™ Mixture Mixed Viscosity (mPas) Specific Weight (g/cm3) Pot Life (min) Cure Time (hrs) Colour Hardness (Shore A) Tensile Strength (N/mm) Elongation at Break (%) Schrinkage (%)
30 1A:1B(Weight) 750 1,03 15 16 clear 30 5 675 ,2
50 1A:2B(Volume) 250 1,04 25 16 clear 50 4,3 500 0,15
95 1A:1,5B(Volume) 250 1,04 25 16 clear 95 35,7 175 0,28

Vytaflex Table

VYTAFLEX® Mixture (by Volume) Mixed Viscosity (mPas) Specific Weight (g/cm⊃3;) Pot Life (min) Cure Time (hrs) Colour Hardness (Shore A) Tensile Strength (N/mm) Elongation at Break (%) Schrinkage (%)
10 1A:1B 3100 1,00 30 24 creme 10 6,8 1000 <0,1
20 1A:1B 1000 1,00 30 16 amberclear 20 10,7 1000 <0,1
30 1A:1B 1800 1,02 30 16 creme 30 13,9 1000 <0,1
40 1A:1B 2000 1,03 30 16 creme 40 14,6 660 <0,1
50 1A:1B 2000 1,04 60 16 creme 50 18,2 400 <0,1
60 1A:1B 2000 1,04 60 16 creme 60 24,3 480 <0,1

Econ 80, Simpact & Urecoat

  Mixture (by Volume) Mixed Viscosity (mPas) Specific Weight(g/cm³) Pot Life (min) Cure Time (hrs) Colour Hardness (Shore A) Tensile Strength (N/mm) Elongation at Break (%) Schrinkage (%)
Econ 80 1A:1B(volume&weight) 1,200 1,06 13 24 translucent 80 5,6 125 ,014
Simpact 85 A 85A:100B(weight) 1,100 1,09 4 48 off-white 85 6,6 165 <,07
Urecoat 100A:10B(weight) 3,800   8 16 translucent amber 70 9,4 875 -