Low-viscosity, clear, silicone rubber for electronic protection.Protects against shock, vibration and moistureUltra-transparent and UV resistantNo solvents or VOCsComplete Cure in deep sections
| Hundred Percent Modulus | 25 psi |
| Color | Clear |
| Mixed Viscocity | 1,200 cps |
| Useful Temperature Min | -149 °F |
| Cure Time | 24 hours |
| Pot Life | 240 minutes |
| Specific Volume | 28.1 cu. in./lb. |
| Specific Gravity | 0.99 g/cc |
| Mix Ratio By Weight | 1A:1B |
| Shrinkage | <.001 in. / in. |
| Dielectric Strength | 366 volts/mil |
| Mix Ratio By Volume | 1A:1B |
| Tensile Strength | 180 psi |
| Elongation At Break | 290 % |
| Dielectric Constant 100hz | 2.780000 |
| Shore A Hardness | 15 |
| Volume Resistivity | 3.16E+15 ohm/cm |
| Dissipation Factor 100hz | 0.000000 |
| Refractive Index | 1.41 nm |
| Thermal Conductivity | 0.18 W/M*K |
Low-viscosity, clear, silicone rubber for electronic protection.Protects against shock, vibration and moistureUltra-transparent and UV resistantNo solvents or VOCsComplete Cure in deep sections
Prepares glass surfaces for effective bonding to optical-clear Solaris™ platinum silicone.Use isopropyl alcohol for initial cleaningFollow with ammonia-based glass cleanerApply two coats of primer10-minute drying time between coatsWipe away hazy film after each coat
| Product | Color | Hundred Percent Modulus | Color | Mixed Viscocity | Useful Temperature Min | Cure Time | Pot Life | Specific Volume | Specific Gravity | Mix Ratio By Weight | Shrinkage | Dielectric Strength | Mix Ratio By Volume | Tensile Strength | Elongation At Break | Dielectric Constant 100hz | Shore A Hardness | Volume Resistivity | Dissipation Factor 100hz | Refractive Index | Thermal Conductivity |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Solaris™ | Clear | 25 psi | Clear | 1,200 cps | -149 °F | 24 h. | 240 min. | 28.1 cu. in./lb. | 0.99 g/cc | 1A:1B | <.001 in. / in. | 366 volts/mil | 1A:1B | 180 psi | 290 % | 2.780000 | 15 | 3.16E+15 ohm/cm | 0.000000 | 1.41 nm | 0.18 W/M*K |
| Solaris™ Bonding Primer™ | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - |