| Product | Cure Time | Shore A Hardness | Specific Gravity | Specific Volume | Color | Tensile Strength | Shrinkage | Elongation At Break | Hundred Percent Modulus | Die B Tear Strength | Useful Temperature Min | Mixed Viscocity | Mix Ratio By Volume | Mix Ratio By Weight | Pot Life | Hundred Percent Modulus | Color | Die B Tear Strength | Mixed Viscocity | Useful Temperature Min | Cure Time | Pot Life | Specific Volume | Specific Gravity | Mix Ratio By Weight | Shrinkage | Mix Ratio By Volume | Tensile Strength | Elongation At Break | Shore A Hardness | Dielectric Strength | Dielectric Strength |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Ecoflex™ 00 10 | 4 h. | 00-10 | 1.04 g/cc | 26.6 cu. in./lb. | Translucent | 120 psi | <.001 in. / in. | 800 % | 8 psi | 22 pli | -65 °F | 14,000 cps | 1A:1B | 1A:1B | 30 min. | 8 psi | Translucent | 22 pli | 14,000 cps | -65 °F | 4 h. | 30 min. | 26.6 cu. in./lb. | 1.04 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 120 psi | 800 % | 00-10 | - | - |
| Ecoflex™ 00 20 | 4 h. | 00-20 | 1.07 g/cc | 26.0 cu. in./lb. | Translucent | 160 psi | <.001 in. / in. | 845 % | 8 psi | 30 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 30 min. | 8 psi | Translucent | 30 pli | 3,000 cps | -65 °F | 4 h. | 30 min. | 26.0 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 160 psi | 845 % | 00-20 | - | - |
| Ecoflex™ 00 20 FAST | 1 h. | 00-20 | 1.07 g/cc | 26 cu. in./lb. | Translucent | 160 psi | <.001 in. / in. | 845 % | 8 psi | 30 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 20 min. | 8 psi | Translucent | 30 pli | 3,000 cps | -65 °F | 1 h. | 20 min. | 26 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 160 psi | 845 % | 00-20 | 350 volts/mil | 350 volts/mil |
| Ecoflex™ 00 30 | 4 h. | 00-30 | 1.07 g/cc | 26.0 cu. in./lb. | Translucent | 200 psi | <.001 in. / in. | 900 % | 10 psi | 38 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 45 min. | 10 psi | Translucent | 38 pli | 3,000 cps | -65 °F | 4 h. | 45 min. | 26.0 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 200 psi | 900 % | 00-30 | - | - |
| Ecoflex™ 00 50 | 3 h. | 00-50 | 1.07 g/cc | 25.9 cu. in./lb. | Translucent | 315 psi | <.001 in. / in. | 980 % | 12 psi | 50 pli | -65 °F | 8,000 cps | 1A:1B | 1A:1B | 18 min. | 12 psi | Translucent | 50 pli | 8,000 cps | -65 °F | 3 h. | 18 min. | 25.9 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 315 psi | 980 % | 00-50 | - | - |
For over thirty years we have sought out the highest quality modelling, moulding and casting materials from around the world.
From silicones and resins to Jesmonite and special effects materials — a curated range for professionals, artists and makers.
Our sales team is widely known for their knowledge and dedication, supporting you in mould making, casting, sculpture and prototyping.
We ship from our warehouses in Amsterdam, Barcelona and Madrid to customers throughout Europe, from Greece up to Norway.
Founded in Amsterdam, FormX grew from a local art foundry into a major European supplier — with our roots firmly in the city.
FormX is specialized in the supply of the highest quality 3D modelling and reproduction materials available and has warehouses and showrooms in Amsterdam, Barcelona and Madrid.