Epoxy products are tailored for a variety of industrial applications, providing robust solutions for professionals in fields such as moldmaking, laminating, and casting. The range includes:
EpoxAcast™ Series: Known for its versatility, these epoxies are solvent-free and VOC-free, offering superior hardness and resistance to heat and abrasion.
EpoxAmite™: A high-performance epoxy resin ideal for moldmaking and composite work, featuring a low-viscosity formula for excellent adhesion and penetration.
EpoxAcoat™: Used as an initial coat in moldmaking, this professional-grade epoxy self-levels and enhances adhesion, reducing air bubbles.
Habitat Cast N Coat™: A two-component epoxy that can be cast solid or applied to vertical surfaces, curing to a durable, flame-resistant finish.
Epsilon Series: Brushable epoxy coatings that enhance EPS foam, providing a durable surface for theming and prop-making.
Additional options include Tarbender, a clear, high-gloss epoxy coating suitable for various substrates, and Plasti-Paste™ EPOXY, a fiber-filled paste for vertical applications. These products are designed to meet the demanding needs of industrial applications, ensuring high performance and reliability.
Clear, high-gloss epoxy coating and encapsulant, for wood, plaster, concrete, foam, fabrics, paper, etc. and to encapsulate 2-D or 3-D objects.
Epoxy-based, fiber-filled epoxy-paste for vertical applications.
| Product | Color | Cure Time | Pot Life | Specific Volume | Specific Gravity | Mix Ratio By Weight | Mix Ratio By Volume | Tack Free Time | Shore D Hardness | Thin Film Working Time | Thin Film Recoat Time | Mixed Viscosity | Color | Mixed Viscocity | Flexural Strength | Flexural Modulus | Shrinkage | Ultimate Tensile | Elongation At Break | Heat Deflection Temp | Compressive Strength | Tensile Modulus | Compressive Modulus |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Tarbender | Clear | 16 h. | 45 min. | 25.4 cu. in./lb. | 1.09 g/cc | 100A:41B | 2A:1B | 8 h. | 75 | 2 h. | 6 h. | 1,100 cps | - | - | - | - | - | - | - | - | - | - | - |
| Plasti-Paste™ EPOXY | Off-White | 16 h. | 40 min. | 27.73 cu. in./lb. | 1.0 g/cc | 2A:1B | 2A:1B | - | 80 | - | 60 min. | - | Off-White | Paste | 9,186 psi | 2,273,000 psi | 0.001 in. / in. | 3,320 psi | 0.83 % | 160 °F | 7,700 psi | 470,000 psi | 138,000 psi |
| UV Resin | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - |