TASK™ Series

Produce high-strength, performance-grade cast components with Smooth-On TASK™ urethane systems. This series includes rigid, semi-rigid, heat-resistant, flame-resistant, aluminum-filled and ABS-like materials with different working times, cure speeds and mechanical properties. Ideal for functional prototypes, tooling, industrial parts, vacuum forming molds, props and demanding production applications.
Available in TASK™ Series
Product Color Color Mixed Viscocity Cure Time Pot Life Flexural Strength Flexural Modulus Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore D Hardness Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus Handling Time Heat Deflection With Post Cure Hundred Percent Modulus Die C Tear Strength Shore A Hardness
TASK™ 2 White White 150 cps 60 min. 7 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.005 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - -
TASK™ 3 White White 150 cps 90 min. 20 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.0025 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - -
TASK™ 4 Ivory Ivory 250 cps 16 h. 20 min. 9,000 psi 204,000 psi 23.9 cu. in./lb. 1.167 g/cc 100A:100B 0.0035 in. / in. - 6,500 psi 4 % 83 110 °F 7,400 psi 130,000 psi 75,000 psi - - - - -
TASK™ 5 Tan Tan 600 cps 24 h. 3 min. 6,480 psi 216,000 psi 25.2 cu. in./lb. 1.1 g/cc 1A:1B 0.007 in. / in. 1A:1B 4,530 psi 5 % 77 145 °F 6,700 psi 200,000 psi 83,000 psi 15 min. - - - -
TASK™ 6 Tan Tan 800 cps 24 h. 7 min. 6,200 psi 182,500 psi 25.9 cu. in./lb. 1.07 g/cc 1A:1B 0.0031 in. / in. 1A:1B 5,200 psi 4 % 75 162 °F 5,570 psi 146,000 psi 65,000 psi 75 min. - - - -
TASK™ 7 Off-White Off-White 200 cps 10 min. 2.5 min. 5,450 psi 148,900 psi 23.1 cu. in./lb. 1.2 g/cc 104A:100B 0.0111 in. / in. 1A:1B 3,390 psi 15.1 % 73 131 °F 5,140 psi 150,700 psi 57,600 psi - - - - -
TASK™ 8 Off-White Off-White 100 cps 15 min. 2.5 min. 8,280 psi 271,000 psi 25.4 cu. in./lb. 1.09 g/cc 120A:100B 0.01 in. / in. 1A:1B 5,840 psi 4 % 80 194 °F 8,760 psi 246,000 psi 77,400 psi - 263 °F - - -
TASK™ 11 Translucent White Translucent White 2,000 cps 16 h. 20 min. - - 24.7 cu. in./lb. 1.12 g/cc 100A:100B 0.0024 in. / in. - 2,500 psi 100 % 60 - - - - - - - - -
TASK™ 12 Clear Amber Clear Amber 2,400 cps 16 h. 20 min. - - 26 cu. in./lb. 1.08 g/cc 100A:44B 0.001 in. / in. - 2,700 psi 300 % 60 - - - - - - - - -
TASK™ 13 Black Black 800 cps 20 min. 3 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.005 in. / in. - 1,800 psi 125 % 50 - - - - - - - - -
TASK™ 14 Black Black 800 cps 45 min. 10 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.0035 in. / in. - 1,800 psi 125 % 50 - - - - - - - - -
TASK™ 15 Opaque White Opaque White 600 cps 1 h. 6 min. 5,450 psi 170,000 psi 24.7 cu. in./lb. 1.12 g/cc 75A:100B 0.0042 in. / in. - 2,720 psi 20 % 75 117 °F 5,450 psi 126,000 psi 60,000 psi - - - - -
TASK™ 16 Light Yellow Light Yellow 1,400 cps 24 h. 6 min. - - 25.64 cu. in./lb. 1.08 g/cc 1A:2B 0.0025 in. / in. - 2,264 psi 233 % 30 - - - - 90 min. - 855 psi 197 pli 80
TASK™ 18 Metal Gray Metal Gray 4,400 cps 16 h. 20 min. 10,700 psi 86,000 psi 17.6 cu. in./lb. 1.57 g/cc 26A:100B 0.0006 in. / in. - 3,250 psi 1 % 88 149 °F 8,420 psi 514,000 psi 97,300 psi - - - - -
TASK™ 21 White White 500 cps 1 h. 6 min. 7,100 psi 250,000 psi 25.9 cu. in./lb. 1.07 g/cc 2A:1B 0.0058 in. / in. 2A:1B 5,500 psi 7.5 % 75 144 °F 7,100 psi 270,000 psi 78,500 psi - - - - -

Why buy at FormX?

Subscribe to our Newsletter

Stay up to date with the latest offers

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
This website has been developed by Usecue B.V.
© 2026 FormX B.V.