EpoxAcoat™ NEUTRAL

EpoxaCoatNeutralx ⓘ 0F8B2C72-3092-1342-AE70-3FAD0BD5432C
Epoxy

Thixotropic epoxy gel coat for hand laminating and tooling.

  • Mix ratio: 5A:1B by volume
  • Cure time: 16 hours at 23°C
  • Shore hardness: 85 D
  • Abrasion-resistant
  • Can be drilled or sanded
exclamation.svg corrosion.svg health-hazard.svg

Warning

H315 - Causes skin irritation.
H317 - May cause an allergic skin reaction.
H319 - Causes serious eye irritation.
H312 - Harmful in contact with skin.
H318 - Causes serious eye damage.
€ 158.20

(€ 130.74 without 21% VAT)

Only 3 available in stock

Description

This thixotropic epoxy resin is designed for creating hard, durable surfaces in composite tooling, molds, master patterns, and fixtures. 

EpoxAcoat™ NEUTRAL serves as a surface or gel coat layer, typically reinforced with fiberglass or other fabrics using compatible laminating epoxies. 

The neutral off-white color is suitable for applications requiring a light base or custom pigmentation.

Specifications

  • Mix Ratio By Volume: 5A:1B
  • Mix Ratio By Weight: 100A:15B
  • Pot Life: 20 minutes
  • Thin Film Working Time: 40 minutes
  • Thin Film Recoat Time: 60 minutes
  • Tack Free Time: 4 hours
  • Cure Time: 16 hours
  • Shore Hardness: 85 D
  • Specific Gravity: 1.43 g/cc
  • Specific Volume: 1.19 cm³/g (19.4 cu. in./lb)
  • Color: Neutral
  • Barcol 935 Hardness: 87
  • Ultimate Tensile: 179.3 MPa (26,000 psi)
  • Flexural Strength: 206.8 MPa (30,000 psi)
  • Compressive Strength: 165.5 MPa (24,000 psi)
  • Heat Deflection Temp: 56°C (133°F)
  • Shrinkage: 0.00015 mm/mm
  • Mixed Viscosity: Light Paste

Instructions

  • Use in a well-ventilated area and avoid inhaling fumes. A NIOSH-approved respirator is recommended.
  • Wear safety glasses, long sleeves, and rubber gloves.
  • Store and use at room temperature (23°C). Elevated temperatures reduce pot life.
  • Do not mix in glass or foam containers and do not apply thicker than 3.2 mm due to exothermic reaction.
  • Measure Parts A and B accurately by volume or weight and mix thoroughly for at least 3 minutes, scraping sides and bottom.
  • Pour into a shallow pan to extend pot life if needed.
  • For nonporous molds, apply a suitable release agent.
  • Apply two thin coats with a brush, allowing each layer to reach a “tacky-hard” stage before applying the next.
  • Reinforce with fiberglass and compatible epoxy systems if required.
  • Cure at 23°C until fully hard, then sand or machine with a dust mask.
  • Mild heat may be used to accelerate cure; allow to cool before handling.
  • Clean uncured epoxy with approved solvents using proper ventilation.

Specifications

Color Neutral
Mixed Viscocity Light Paste
Cure Time 16 hours
Flexural Strength 30,000 psi
Pot Life 20 minutes
Specific Volume 19.4 cu. in./lb.
Specific Gravity 1.43 g/cc
Mix Ratio By Weight 100A:15B
Shrinkage 0.00015 in. / in.
Mix Ratio By Volume 5A:1B
Tack Free Time 4 hours
Ultimate Tensile 26,000 psi
Shore D Hardness 85
Heat Deflection Temp 133 °F
Thin Film Working Time 40 minutes
Compressive Strength 24,000 psi
Thin Film Recoat Time 60 minutes
Barcol 935 Hardness 87.000000
Available in Epoxy
Product Color Color Mixed Viscocity Cure Time Flexural Strength Pot Life Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tack Free Time Ultimate Tensile Shore D Hardness Heat Deflection Temp Thin Film Working Time Compressive Strength Thin Film Recoat Time Barcol 935 Hardness
EpoxAcoat™ GREY Grey Grey Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
EpoxAcoat™ NEUTRAL Neutral Neutral Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
EpoxAcoat™ RED Red Red Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
EpoxAcoat™ WHITE White White Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
Recommended products

Why buy at FormX?

Subscribe to our Newsletter

Stay up to date with the latest offers

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
This website has been developed by Usecue B.V.
© 2026 FormX B.V.