EpoxAcoat™ GREY

EpoxAcoatGreyx ⓘ 360431B2-5011-E448-BD02-A264D77662DD
Epoxy

Thixotropic epoxy gel coat with high abrasion resistance.

  • Shore Hardness: 85 D
  • Mix Ratio: 5A:1B by volume
  • Pot Life: 20 minutes
  • Ultimate Tensile: 179 MPa (26,000 psi)
  • Heat Deflection Temp: 56°C (133°F)
exclamation.svg corrosion.svg health-hazard.svg

Warning

H315 - Causes skin irritation.
H317 - May cause an allergic skin reaction.
H319 - Causes serious eye irritation.
H312 - Harmful in contact with skin.
H318 - Causes serious eye damage.
€ 187.31

(€ 154.80 without 21% VAT)

In stock

Description

This thixotropic epoxy gel coat is used for hand laminating and tooling applications. It cures at room temperature, providing strong abrasion resistance. The series includes variants for different applications, such as adding color pigments or high-temperature use.

Features

  • Easy application on various surfaces without sagging.
  • Allows for fiberglass cloth lamination for strong, lightweight tools.
  • Machines precisely without chipping.
  • Suitable for precision tooling, master and pattern making, core boxes, and fixtures.

Technical Properties

  • Mix Ratio By Volume: 5A:1B
  • Mix Ratio By Weight: 100A:15B
  • Specific Gravity: 1.43 g/cc
  • Specific Volume: 0.70 cm³/g (19.4 cu. in./lb.)
  • Pot Life: 20 minutes
  • Thin Film Working Time: 40 minutes
  • Thin Film Recoat Time: 60 minutes
  • Tack Free Time: 4 hours
  • Cure Time: 16 hours
  • Shore Hardness: 85 D
  • Barcol 935 Hardness: 87
  • Color: Grey
  • Ultimate Tensile: 179 MPa (26,000 psi)
  • Flexural Strength: 207 MPa (30,000 psi)
  • Compressive Strength: 165 MPa (24,000 psi)
  • Heat Deflection Temp: 56°C (133°F)
  • Shrinkage: 0.00015 mm/mm
  • Mixed Viscosity: Light Paste

Instructions

Use in a well-ventilated area and wear protective gear. Avoid using glass or foam containers due to high exotherm. Store and use at room temperature (23°C/73°F).

Preparation

  • Use a NIOSH approved respirator and safety glasses.
  • Mix components thoroughly for full cure properties.
  • Test a small application for suitability.

Applying A Release Agent

Use Ease Release™ 200 or 205 for nonporous surfaces to prevent adhesion.

Measuring / Dispensing

Accurate measurements by volume or weight are crucial. Use clean containers.

Adding Color

Mix UVO™ color tints with Part A before adding Part B.

Mixing

Mix Parts A and B for at least 3 minutes, scraping sides and bottom. Use a shallow pan to extend pot life.

Adding Fillers

Pre-mix dry fillers with Part A before adding Part B.

Important

Mixed material generates heat. Avoid thick applications and use appropriate containers.

Applying

Apply two thin layers with a chip brush. Allow each layer to partially cure before applying the next.

Cure Time

Refer to specified cure times. Cured material can be sanded. Use a mask when sanding.

Heat Curing

Room temperature cure is sufficient, but mild heat can reduce cure time.

Painting

Cured material can be painted with acrylic enamel paints.

Removing Epoxy

Scrape uncured epoxy and clean residue with appropriate solvents.

Specifications

Color Grey
Mixed Viscocity Light Paste
Cure Time 16 hours
Flexural Strength 30,000 psi
Pot Life 20 minutes
Specific Volume 19.4 cu. in./lb.
Specific Gravity 1.43 g/cc
Mix Ratio By Weight 100A:15B
Shrinkage 0.00015 in. / in.
Mix Ratio By Volume 5A:1B
Tack Free Time 4 hours
Ultimate Tensile 26,000 psi
Shore D Hardness 85
Heat Deflection Temp 133 °F
Thin Film Working Time 40 minutes
Compressive Strength 24,000 psi
Thin Film Recoat Time 60 minutes
Barcol 935 Hardness 87.000000
Available in Epoxy
Product Color Color Mixed Viscocity Cure Time Flexural Strength Pot Life Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tack Free Time Ultimate Tensile Shore D Hardness Heat Deflection Temp Thin Film Working Time Compressive Strength Thin Film Recoat Time Barcol 935 Hardness
EpoxAcoat™ GREY Grey Grey Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
EpoxAcoat™ NEUTRAL Neutral Neutral Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
EpoxAcoat™ RED Red Red Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
EpoxAcoat™ WHITE White White Light Paste 16 h. 30,000 psi 20 min. 19.4 cu. in./lb. 1.43 g/cc 100A:15B 0.00015 in. / in. 5A:1B 4 h. 26,000 psi 85 133 °F 40 min. 24,000 psi 60 min. 87.000000
Recommended products

Why buy at FormX?

Subscribe to our Newsletter

Stay up to date with the latest offers

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
This website has been developed by Usecue B.V.
© 2026 FormX B.V.